Hydrogen Storage Electrode Legierungs Pulvern

Type

C

L

T

S

E

Molekulare Formel 

ABx

ABx

ABx

ABx

ABx

x=5.1±0.10

x=5.1±0.10

x=4.85±0.10

x=5.15±0.10

x=5.25±0.10

 Major elements

Mm(TRE)(%)

32.7±1.0

32.6±1.0

34.0±1.0

32.4±1.0

32.2±1.0

Co(%)

10.0±0.5

10.0±0.5

10.2±0.5

5.0~9.0

3.0~7.0

Impurities (%)

O

≤0.1

≤0.1

≤0.1

≤0.1

≤0.1

Fe

≤0.1

≤0.1

≤0.1

≤0.1

≤0.1

Mg

≤0.03

≤0.03

≤0.03

≤0.03

≤0.03

Zn

≤0.02

≤0.02

≤0.02

≤0.02

≤0.02

Ca

≤0.02

≤0.02

≤0.02

≤0.02

≤0.02

C

≤0.02

≤0.02

≤0.02

≤0.02

≤0.02

Pb

≤0.02

≤0.02

≤0.02

≤0.02

≤0.02

Electrochemical Property

Cycle life (100%DOD)

≥500

≥600

≥400

≥500

≥500

Electrochemical capacity

≥320mAh/g

≥310mAh/g

≥300mAg/g

≥320mAh/g

≥300mAh/g

Voltage flat(1.2V/1.0V)

≥80%

≥80%

≥85%

≥80%

≥80%

Eigenschaft von Wasserstoff absorbiert und Loslassen

Hydrogen Absorptionsfähigkeit(Hab/m)

10atm

>0.90H/M

>0.90H/M

>0.85H/M

>0.90H/M

>0.85H/M

3atm

>0.80H/M

>0.80H/M

>0.65H/M

>0.80H/M

>0.78H/M

Equilibrium Wasserstoffdruck(at H/M=0.4)

0.4±0.1atm

0.35±0.1atm

1.3±0.1atm

0.5±0.1atm

0.45±0.1atm

Plateau Property

≤0.5

≤0.5

≤0.5

≤0.5

≤0.5

Empfehlen Gebräuche

Geeignet zur Herstellung von Hochleistungs-Akku

Geeignet zur Herstellung lange Lebensdauer Batterie

Geeignet zur Herstellung von Akkus bei niedrigen Temperaturen

Geeignet zur Herstellung von Power Akku

Geeignet zur Herstellung von wirtschaftlichen Batterie